The effects of Ta addition on the magnetic properties of permalloy thin films have been investigated. The alloy compositions on a weight basis are (Ni₈₁Fe₁₉)_1-x Ta _x with 0 x 0.105, and the films are sputtered onto a glass substrate at between room temperature and 300 C. The saturation magnetization and anisotropic magnetic field decrease with increasing Ta content. The saturation magnetization is 0.75 T at 5 wt % Ta. The coercivity remains constant at 125 Am^-1. The electrical resistivity increases linearly with increasing Ta content, then saturates at approximately 7.5 wt% Ta. The saturation resistivity is approximately 1.00 m. The magnetoresistivity ratio (/) decreases with increasing Ta content, mainly due to increased electrical resistivity (). The magnetostriction changes from negative to positive with increasing Ta content and reaches nearly zero at 2 wt% Ta. The NiFeTa films containing 5–6 wt% Ta have potential for use as the soft-biasing film in magnetoresistive elements.