This study deals with the determination of uniaxial tensile strength of concretes reinforced with
A-fibres (slag-basalt fibres) and glass-fibres at the age of 0,3 and 6 hours. For the determination of the tensile strength
of fibre-reinforced concrete in its early age of setting and hardening a method was applied which was developped for the investigation
of plain concretes.
Tests were performed to obtain the relationships between the fibre volume fractions and uniaxial tensile strengths of concretes
at different, ages. The kinetics of strength increase has been studied. It is shown that the kinetics of strength increase
is to a high degree dependent on the kind of fibre reinforcement.
Dans le cas de fibres A (laitier basaltique), la résistance à la traction des bétons armés par 3,5% de fibres en volume était,
à toutes les étapes du durcissement (0,3 et 6 heures), à peu près de 2 k Nm
−2 supérieure, à celle des bétons contenant 1,25% de fibres. Par rapport à la matrice béton, le gain est de 4 kNm
−2 pour les bétons armés de 3,5% de fibres à 3 heures aussi bien, qu'à 6 heures.
Dans le cas de bétons armés de fibres de verre, le gain de résistance n'est plus constant en fonction du temps, la différence
de résistance entre les bétons ayant le plus faible pourcentage volumique de fibres, 0,75%, et le plus élevé, 2,5%, croît
avec l'âge du béton. Les différences observées sont de 2 k Nm−2 à 3 heures et de 7 kNm−3 à 6 heures après coulage. La comparaison entre matrice béton et béton armé de 2,5% de fibres est la suivante: à 3 heures
la différence est de 4 kNm−2 et approximativement 13 kNm−2 à 6 heures.