The hafnium and silicon precursors, Hf(NMe₂)₄ and Bu^tMe₂SiOH, have been investigated for the MOCVD of high- hafnium silicate, (HfO₂)_1–x –(SiO₂) _x films for gate dielectric applications. Control of the silica concentration in the hafnium silicate can be achieved by varying the relative precursor ratios up to a saturation level of 35–40% SiO₂. The thermal stability of the resulting hafnium silicate films in air has been investigated using medium energy ion scattering. Internal oxidation of the underlying silicon substrate is discernable when the films are annealed in dry air for 15 min over the temperature range 800–1000 °C.