The present work represents a thermal study of synthesis of cryptohalite (Ammonium silicon hexafluoride) by sintering of quartz with ammonium fluoride using a derivatograph. The reaction products were identified microscopically and by using a Siemens Crystalloflex diffractometer. The DTA curves indicate that the intensive formation of cryptohalite takes place at 125
–155
C by an endothermic reaction. Cryptohalite is unstable and dissociates at 320
–335
C as represented by the sharp and large endothermic peaks at these temperatures.
The resulted cryptohalite is colorless in thin sections and crystallizes in cubic system, in the form of octahedral crystals with perfect (111) cleavage. The dimorph bararite is not detected in all runs.
Mittels eines Derivatographen wurde die Synthese von Kryptohalit (Ammoniumsiliziumhexafluorid) durch Sintern von Quarz mit Ammoniumfluorid thermisch untersucht. Die Reaktionsprodukte wurden mikroskopisch und mit Hilfe eines Siemens-Crystalloflex Diffraktometers identifiziert. Die DTA-Kurven zeigen, da\ die intensive Bildung von Kryptohalit in einer endothermen Reaktion bei 125
–155
C abläuft. Wie durch die scharfen und intensiven endothermen Peaks bei 320
–335
C gezeigt wird, ist Kryptohalit bei dieser Temperatur instabil und dissoziiert.
Das erhaltene Kryptohalit ist in dünnen Schnitten farblos und kristallisiert im kubischen System in der Form von oktaedrischen Kristallen mit perfekter (111) Spaltbarkeit. Das dimorphe Bararit konnte in keinem der Versuche beobachtet werden.
Keywords synthesis of cryptohalite - DTA - Crystalloflex diffractometer