The crystal structures of synthetic CuSO
4 and ZnSO
4 were refined to R=0.048, 0.037 (R
w = 0.039, 0.035) using single crystal X-ray data up to sin
/
= 0.8 Å
–1. Space group Prima, cell parameters: a=8.409(1), 8.604 (5) Å; b=6.709(1), 6.746 (5) Å; c=4.833 (1), 4.774 (3) Å; Z =4. The refinements essentially confirmed the atomic arrangements of earlier works, but the atomic parameters could be determined with considerably higher accuracy.
The Me
2+ atoms are coordinated to six O atoms forming distorted octahedra; the Zn atom has a [2 + 2 – 2] coordination, whereas the Cu atom tends to a [4 + 2] coordination. These
octahedra
share edges to build chains parallel to [010], which are connected to a framework by SO
4 tetrahedra.
Die Kristallstrukturen von synthetischem CuSO
4 und ZnSO
4 wurden unter Verwendung von Einkristallröntgendaten im Bereich bis sin
/
= 0.8 Å
–1 zu R-Werten von 0.048, 0.037 (R
w =0.039, 0.035) verfeinert. Raumgruppe Pnma, Zellparameter: a= 8,409 (1), 8,604 (5) Å; b=6,709(1), 6,746 (5) Å; c=4,833(1), 4,774 (3) Å; Z=4. Die Verfeinerungen bestätigten im wesentlichen die Atomanordnungen früherer Arbeiten, die Atom-parameter konnten jedoch mit wesentlich höherer Genauigkeit bestimmt werden.
Die Me
2+ Atome sind von sechs Sauerstoffatomen umgeben und bilden verzerrte Oktaeder. Das Zn Atom besitzt eine [2 + 2 + 2] Koordination, das Cu Atom tendiert eher zu einer [4+2] Koordination. Diese
Oktaeder
sind über Kanten zu Ketten parallel [010] verknüpft, die durch SO
4 Tetraeder zu einer Gerüststruktur verbunden sind.